Water-reducing agent solution for these three
If you are looking for high-quality products, please feel free to contact us and send an inquiry, email: brad@ihpa.net
The water-reducing agent should be used with concrete admixture, which will reflect the water-reducing effect. Cement quality is therefore a direct factor of the water reducing agent.
The following strategies are to be used when encountering "problem" cements:
High alkali cement
High-alkali is a cement type with a large amount of alkali. Alkali in high-alkali is usually higher than that of conventional cement.
The high-alkali cements have a high degree of alkalinity. This can impact the performance. High-alkali Cement can encourage the setting reaction, which is beneficial to the early development of strength in concrete. High-alkali Cement can also increase the fluidity of cement, making it more workable and easier to pump.
But there are also some issues with high-alkali clinkers. As an example, high alkali cements can reduce the efficiency of water-reducing agents and cause concrete to lose its slump faster. High-alkali cement may also lead to corrosion and carbonation problems in the concrete.
High-alkali Cement can benefit from water-reducing agents that contain a higher content of sodium sulfate. High-alkali cement contains a high amount of alkali, which accelerates C3A's dissolution. Sodium sulfate reacts with C3A, forming AFt crystalline structures and improving the fluidity of the cement mortar.
Low-alkali sulfur-deficient cement
Low alkali-sulfur cement is a cement with a lower sulfate level than normal cement. Ordinary cement is high in sulfate. It reacts with water and the sulfate forms crystals that cause cracks in concrete.
Reduced sulfate cement reduces the impact of the Alkali-Silica reaction in concrete (Alkali-aggregate Reaction) by reducing its sulfate contents. Alkali and silica react in concrete, causing cracking and expansion. The use of low-alkali cements that are sulfur-deficient can help reduce this reaction, and increase the durability and life of the concrete.
Due to the lower sulfate contents, water reducers work less well with low alkali-sulfur cement. Water-reducing agents can cause concrete to lose slump quickly if they are used in excess. In this case, the conventional method of using water-reducing agents may not work. Instead, it is best to choose a water reducing agent that contains sulfate.
High C3A Content Concrete
Cement that has a high C3A level is one with a higher content of C3A. C3A is a mineral present in cement, which when combined with water forms an expansive substance. Cements with a high C3A percentage have a faster setting time and higher early strength. They are ideal for projects requiring rapid strength development and rapid setting.
Cement with high C3A levels can cause some problems. C3A and sulfate react to form sulphoaluminate. This can cause concrete to expand or crack. In humid environments, high C3A cements can produce corrosive Calcium Sulfate Precipitates, which may affect the durability of concrete and steel structures.
Cement containing high C3A has a higher adsorption rate of water-reducing agents. This will result in fewer fluidity and slump properties of concrete. If you are using water-reducing agents, choose a water reducer containing high sulfate content or a slowing agent with hydroxycarboxylate. These will help to reduce C3A adsorption and improve concrete fluidity.
There are two types of products that reduce water: one is the naphthalene product, and another is polycarboxylic acids. The main difference in water reduction is naphthalene. It is high-performance, whereas, polycarboxylic is high-efficiency. For general foam concrete, the naphthalene cubic addition is between a few hundred to a kilo.